EN10025-6 S550Q steel plates is belong to EN10025-6 hot rolled products of structural steels Technical delivery conditions for flat products of high yield strength structural steels in the quenched and tempered condition
The S550Q steel making process shall be in accordance with EN 10025-1. If specified at the time of the order the steel making process shall be reported to the purchaser.
The S550Q steels specified in this document shall be fully killed. The steels shall have a fine grain structure containing nitrogen binding elements in amounts sufficient to bind the nitrogen.
The S550Q designation shall consist of:
− the number of this document (EN 10025-6);
− the steel name or the steel number; the steel name consisting of:
− the symbol S (for structural steel);
− the indication of the minimum specified yield strength for thickness ≤ 50 mm expressed in MPa1);
− the delivery condition Q;
− the capital letter L or L1 for the quality with specified minimum values of impact energy at temperatures not lower than -40 °C or -60 °C.
EXAMPLE S460 Structural steel (S) with a specified minimum yield strength at ambient temperature of 460 MPa1), in the quenched and tempered delivery condition (Q) :
Steel EN 10025-6 – S550Q
When S550Q products are supplied with a control on Si e.g. for hot-dip zinc-coating so that there could be a need to increase the content of other elements like C and Mn to achieve the required tensile properties, the maximum carbon equivalent values of Table 4 shall be increased as follows:
− for Si ≤ 0,030 %, increase CEV by 0,02 %;
− for Si ≤ 0,25 %, increase CEV by 0,01 %.
S550Q sheets Tolerances on dimensions and shape shall be in accordance with the requirements given in the order by reference to the relevant documents according to 2.2 and according to 2.2 and 7.7.1 of EN 10025-1:2004.
For hot rolled plate tolerances the basic requirements shall be in accordance with EN 10029, including thickness tolerances to class A, unless otherwise agreed at the time of the order.
EN10025-6 S550Q Chemical Composition
|
Grade |
Chemical Composition |
|
S550Q |
The Element Max (%) |
|
C |
Si |
Mn |
P |
S |
Nb |
V |
Ti |
Zr |
Cr |
Ni |
Mo |
Cu |
N |
|
0.22 |
0.86 |
1.80 |
0.030 |
0.017 |
0.07 |
0.14 |
0.07 |
0.17 |
1.60 |
2.1 |
0.74 |
0.55 |
0.016 |
EN10025-6 S550Q Mechanical Property
|
Grade |
Mechanical Property |
|
S550Q |
Yield Strength
mm
Min(Mpa) |
Tensile Strength
mm
Min(Mpa) |
Elongation
Min,%
|
|
≥
3
≤
50 |
＞
50
≤
100 |
＞
100
≤
150 |
≥
3
≤
50 |
＞
50
≤
100 |
＞
100
≤
150 |
|
550 |
530 |
490 |
640-820 |
590-770 |
16 |
For the S550Q,the yield strength is 550Mpa，tensile strength is 640-820 Mpa,and its elongation is min 16%.
Which mill produce the S550Q have best quality,Katalor can give you a uniqueness quality products as well as best service.If you want this S550Q material,please consult here for more information.