SUS304L steel grade is a austenitic series stainless steel designed under JIS G4304.
JIS G4304/4312 SUS 304L stainless steel are produced in hot rolled plates, sheets and strips.
JISG4304/4312 SUS 304L stainless steel chemical composition
|
Grade |
C |
Si |
Mn |
P |
S |
Ni |
Cr |
Mo |
|
SUS 304L |
≤0.03 |
≤1.00 |
≤2.00 |
≤0.045 |
≤0.030 |
9-13 |
18-20 |
- |
JISG4304/4312 SUS 304L stainless steel mechanical properties
|
Grade |
Yield strength |
Tensile strength |
Elongation % |
Hardness |
|
HB≤ |
HRB≤ |
HV≤ |
|
SUS 304L |
≥175 |
≥480 |
≥40 |
187 |
90 |
200 |
JIS G4304/4312 SUS 304L stainless steel manufacturing
JIS G4304/4312 SUS 304L stainless steel plates and strips shall be heat treated after hot-rolling and given acid pickling or an equivalent treatment. As required, leveling, grinding or a combination of these treatments may be performed. Treatments such as acid pickling to be performed after heat treatment may be omitted upon agreement between the purchaser and the manufacturer.
Additional Condition :
UT (Ultrasonic examination), AR(As Hot Rolled only), CR(Cold rolled only) N (Normalized), Q+T (Quenched and Tempered), Polish, Pickling, Solution Treatment (Solid Solution), Annealing, The Third Party Test (Such as SGS Test). Classification society inspection include (ABS,CCS,NK,KR,DNV,BV,LR,GL,RINA)
JIS G4304/4312 SUS 304L stainless steel can be used for pipes and furnace parts, muffles, heat exchangers, retorts, elbows, headers exhaust systems, electrodes of ignition spark plugs, welding machines and containers of chemical engineering, operating at t from -196 to 600°C in media active substance.