ASTM A203 Grade E pressure containing parts

The maximum thickness of A203 Grade E pressure plates is limited only by the capacity of the composition to meet the specified mechanical property requirements, however, current practice normally limits the maximum thickness of A203 Grade E boiler plates furnished under 100 mm.
If approved by the purchaser for A203 Gr. E pressure containing parts, cooling rates faster than air cooling are permissible for improvement of the toughness, provided the plates are subsequently tempered at not less than 1100℉[595℃] for not less than ½ h.
[email protected]
0086-21-61182423
Live Chat  Leave a Message

ASTM A203 Grade E Boiler steel usually used to build domestic boiler, industrial boiler, and power station boiler. Boiler steel plates have the good strength.

 

ASTM A203 Grade E pressure containing parts chemical composition:

Grade

C

Mn

P

S

Si

Ni

A203 Grade E

0.20-0.23

0.88

0.025

0.025

0.13-0.45

3.18-3.82

 

ASTM A203 Grade E Boiler steel mechanical properties:

Grade

Tensile Strength MPa (ksi)>

Yield Strength MPa (ksi)

% Elongation in 8 in.(200mm) min

% Elongation in 2 in.(50mm) min

A203 Grade E

485-620 (70-90)

275 (40)

17

21

 

The maximum thickness of A203 Grade E pressure plates is limited only by the capacity of the composition to meet the specified mechanical property requirements, however, current practice normally limits the maximum thickness of A203 Grade E boiler plates furnished under 100 mm.

If approved by the purchaser for A203 Gr. E pressure containing parts, cooling rates faster than air cooling are permissible for improvement of the toughness, provided the plates are subsequently tempered at not less than 1100℉[595℃] for not less than ½ h.