ASTM A662 Grade C steel plate

ASTM A662, as a kind of low alloy steel, chemical composition difference of the 3 steel grades is mainly for Mn element, increasing of Mn content in steel plate will improve yield and tensile strength character.
[email protected]
0086-21-61182423
Live Chat  Leave a Message

ASTM A662 standard specification for pressure vessel plates, carbon-manganese-silicon steel, for moderate and lower temperature service.

ASTM A662, as a kind of low alloy steel, chemical composition difference of the 3 steel grades is mainly for Mn element, increasing of Mn content in steel plate will improve yield and tensile strength character.

Steel Grade

Mn %

ASTM A662 Grade A

0.84-1.46

ASTM A662 Grade B

0.79-1.62

ASTM A662 Grade C

0.92-1.72

ASTM A662 Grade C chemical composition:

Grade

C

Mn ≥

Si

P

S

A662 Grade C

0.24

0.13-0.45

0.79-1.62

0.035

0.035

ASTM A662 Grade C mechanical properties:

Grade

Tensile Strength(MPa)

Yield Strength(MPa)

% Elongation in 2 in.(50mm) min

Impacting Test  Temperature(°C)

A662 Grade C

480-620

295

20

-20,40,-60

ASTM A662 Grade C Equivalent Steel Grade:

ASTM

EN10028

JIS

ISO

A662-C

-

G3115-SGV315

P315

ASTM A662 plates over 40mm in thickness shall be normalized. Plates of Grades B and C, 40 mm and under in thickness, are normally supplied in the as-rolled condition. The plates may be ordered normalized or stress relieved, or both.

If you need more detail information of ASTM A662 Grade C, don’t hesitate to contact us.