Hot rolled steel plate S355J2 is a micro alloyed structural steel suitable for e.g. mechanical engineering applications. Hot rolled steel plate S355J2 posess a good weldability with max CEV =0.47. Hot rolled steel plate S355J2 may be delivered with a controlled silicon content for good galvanazing properties. Below, hot rolled steel plate S355J2 properties are presented.
Hot rolled steel plate S355J2 properties - S355J2 yield strength:
It shows reduction in S355J2 yield strength based on thickness
Up to 16 mm - 355 Mpa
16 mm < t ≤ 40 mm - 345 Mpa
40 mm < t ≤ 63 mm - 335 Mpa
63 mm < t ≤ 80 mm - 325 Mpa
80 mm < t ≤ 100 mm - 315 Mpa
100 mm < t ≤ 150 mm - 295 Mpa
Hot rolled steel plate S355J2 properties - S355J2 tensile strength:
S355J2 ultimate tensile strength ranges also varies based on thickness.
Up to 3 mm - 510 Mpa to 680 Mpa
3 mm < t ≤ 100 mm - 470 Mpa to 630 Mpa
100 mm < t ≤ 150 mm - 450 Mpa to 600 Mpa
Hot rolled steel plate S355J2 is low alloy structural steel with good mechanical properties, low temperature performance, plasticity and good weldability. Hot rolled steel plate S355J2 is one kind of EN standardized low alloy, medium tensile strength steel. Hot rolled steel plate S355J2 is reliable material for many critical structural applications.